Magnet Shape: Rod / Cylinder / Cylindrical
Material: Hard Ferrite (Ceramic)
Coating: No Coating
Grade(Chinese Stardard): Y10T
Detailed magnetic properties data:
Residual Magnetic Flux Density (Br): 3.8-4.0 KGs (mT): 380-400 mT
Intrinsic Coercivity Force (Hcj): 2.89-3.46 KOe 230-275 KA/m
Coercivity Force (Hcb): 2.95-3.65 KOe 235-290 KA/m
Energy Density (BH)max: 3.4-4.0 MGOe 27.0-32.0 KJ/m³
Operating Temperature: -40 °C to +250 °C
Magnetisation Direction: Axial / Radially magnetized
Size (Can be customized according to customer drawings):
Outside Diameter(D): 40 mm
Length(L): 60 mm
Tolerance: +/-2% mm
Delivery time 7-25 days
Measurements
Ceramic (Ferrite) Magnets are produced by calcining a mixture of iron oxide and strontium carbonate to form a metallic oxide. A multiple stage milling operation reduces the calcined material to a small particle size. The powder is then compacted in a die by one of two methods. In the first method, the powder is compacted dry which develops an isotropic magnet with weaker magnetic properties, but with better dimensional tolerances. Often times a dry pressed magnet does not require finish grinding. In the second method, the powder is mixed with water to form slurry. The slurry is compacted in a die in the presence of a magnetic field. The applied field creates an anisotropic magnet which exhibits superior magnetic properties, but usually requires finish grinding.