Magnet Shape: Ball / Sphere
Material: Hard Ferrite (Ceramic)
Coating: No Coating
Grade(USA Stardard): C1
Detailed magnetic properties data:
Residual Magnetic Flux Density (Br): 2.30 KGs (mT): 230 mT
Intrinsic Coercivity Force (Hcj): 1.86 KOe 148 KA/m
Coercivity Force (Hcb): 3.50 KOe 258 KA/m
Energy Density (BH)max: 1.05 MGOe 8.36 KJ/m³
Operating Temperature: -40 °C to +250 °C
Magnetisation Direction: Axial / Radially magnetized
Size (Can be customized according to customer drawings):
Diameter(D): 5 mm
Tolerance: +/-2% mm
Delivery time 7-25 days
Measurements
Ferrite magnet
1,Widely application
2,ISO/TS16949:2009
3,Good quality and competitive price
4,Excellent service
The raw material, iron oxide, for these magnets is mixed with either strontium or barium and milled down to a fine powdered form. The powder is then mixed with a ceramic binder and magnets are produced through a compression or extrusion molding technique that is followed by a sintering process. The nature of the manufacturing process results in a product that frequently contains imperfections such as cracks, porosity, chips, etc. Fortunately, these imperfections rarely interfere with a magnet's performance.